Undersøgelse af mikrostruktur og mekaniske egenskaber af 1,5 mm Ti-6Al-4V titanlegering lasersvejset samling

Nøgleord:Ti-6Al-4V titanlegering/ lasersvejsning / mikrostruktur / mekaniske egenskaber

Forfattere: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong osv.

Shenyang Aircraft Industry Group Co., Ltd

Kilde: svejsning og skæring

Abstrakt: eksperimentet med lasersvejsning plus overflademodifikationssvejsning på 1,5 mmTi-6Al-4V titanlegering was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Sammenføjningens mekaniske egenskaber viser, at trækstyrken og forskydningsstyrken er ækvivalent med basismetallet, og den mindste bøjningsvinkel er 35 grader, hvilket indikerer, at samlingen kan anvendes i teknik.

Morfologi af Ti-6Al-4V titanlegering svejsesamling

Mikrostruktur af svejsezone

Mikrostrukturmorfologi af forskellige regioner i varmepåvirket zone

Testværdi af leds mekaniske egenskaber

Den gennemsnitlige værdi af de mekaniske egenskaber af leddet